EutecTrode Xuper NucleoTec 2222 welding electrodes
Fully alloyed cored wire electrode for joining thick sections with lower preheating and Maximum Safety Margin.
Features and benefits
- With proprietary formulation for maximum safety margin welding crack repairs on thick section parts of low alloy or air-hardenable steels.
- Also developed for safe, reliable joints between ferrous & non-ferrous metals in dissimilar combinations eg. carbon / high alloy / stainless steels, various nickel & copper based alloys.
- Reliable weld metallurgical properties retained from cryogenic to refractory temperatures.
- Unique plastic ductility properties minimise harmful residual stresses and distortion.
- Exceptional resistance to fatigue cracks caused by stress raisers or thermal cycles.
- Coefficient of thermal expansion similar to steel reduces welding stresses.
- Maximum resistance to hydrogen induced cold cracking defects.
- Highest dilution tolerance for Fe, Cr, Ni, Mn, C, Cu.
- Thermal shocks do not embrittle the weld deposit structure.
- Suitable for service in corrosive or high temperature environments.
- Economises costly preheating and Post Weld Heat Treatment procedures.
Beschrijving
Features and benefits
- With proprietary formulation for maximum safety margin welding crack repairs on thick section parts of low alloy or air-hardenable steels.
- Also developed for safe, reliable joints between ferrous & non-ferrous metals in dissimilar combinations eg. carbon / high alloy / stainless steels, various nickel & copper based alloys.
- Reliable weld metallurgical properties retained from cryogenic to refractory temperatures.
- Unique plastic ductility properties minimise harmful residual stresses and distortion.
- Exceptional resistance to fatigue cracks caused by stress raisers or thermal cycles.
- Coefficient of thermal expansion similar to steel reduces welding stresses.
- Maximum resistance to hydrogen induced cold cracking defects.
- Highest dilution tolerance for Fe, Cr, Ni, Mn, C, Cu.
- Thermal shocks do not embrittle the weld deposit structure.
- Suitable for service in corrosive or high temperature environments.
- Economises costly preheating and Post Weld Heat Treatment procedures.
Gerelateerde documenten
Technische Data
Tensile strength Rm at 20°C
~670 MPa
Yield strength Rp0.2 at 20°C
~390 MPa
Elongation A5 at 20°C
~45 %
Impact strength ISO-V at 20°C
~130J